@article { author = {Nakhaei, Mohammadreza and Madani, Azam Sadat and Ansari Astaneh, Pedram and Bagheri, Hossein and Alavi, Samin}, title = {Influence of Silica-Lasing Method on the Bond Strength of Composite Resin to Ni-Cr Alloy: Comparison of CO2 and Nd:YAG Lasers}, journal = {Journal of Mashhad Dental School}, volume = {40}, number = {1}, pages = {83-92}, year = {2016}, publisher = {Mashhad University of Medical Sciences, School of Dentistry}, issn = {1560-9286}, eissn = {2008-2347}, doi = {10.22038/jmds.2016.6337}, abstract = {Introduction: In this study silica-coated alumina particles (Cojet sand) were irradiated by CO2 laser and Nd:YAG laser with the intention of  stabilization on the metal surface and bond strength to composite resin was evaluated. Materials & Methods: Forty Ni-Cr cylindrical specimens were fabricated. The bonding surface of all specimens was airborne-particle abraded using 50 µm aluminum oxide particles. Specimens were divided into four groups that received the following surface treatments: 1-airborne-particle abrasion alone (A.A); 2- airborne-particle abrasion with Cojet sand; 3-metal surface coated with Cojet sand and irradiated by Nd:YAG laser (CJ-Lased-Nd:YAG); 4- metal surface coated with Cojet sand and irradiated by CO2 laser (CJ-Lased-CO2). Composite resin was applied on metal surfaces. Specimens were thermocycled and tested in shear mode in a universal testing machine. The mode of failure was determined, and two specimens in each group were examined by scanning electron microscopy and wavelength dispersive X-ray spectroscopy. The shear bond strength values were analyzed using ANOVA and Tukey’s tests (α=0.05). Results: Si-CO showed significantly higher shear bond strength in comparison to other groups (P<0.001). There was no significant difference among groups A.A, CJ-Lased-Nd:YAG and CJ-Lased-CO2 (P>0.05). In Si-CO group, the failure mode was mostly cohesive; but other groups showed adhesive failure in the metal-composite interface. Conclusion: Silica-lasing with Cojet sand and irradiation of Nd:YAG or CO2 laser is not an effective method in improving  metal-composite bond strength.}, keywords = {Silica-coating,Silica-lasing,Nd:YAG laser,CO2 laser,Bond Strength,Composite Resin}, title_fa = {اثر روش سیلیکا لیزینگ بر روی استحکام باند کامپوزیت رزین به آلیاژ نیکل- کروم: مقایسه لیزرهای CO2 و Nd:YAG}, abstract_fa = {مقدمه: در این مطالعه ذرات آلومینای پوشیده با سیلیکا (پودر Cojet)  با هدف تثبیت روی سطح فلز تحت تابش دو نوع  لیزر CO2 و Nd:YAG قرار گرفتند (سلیکالیزینگ) و استحکام باند برشی آنها با کامپوزیت بررسی شد. مواد و روش ها: 40 نمونه دیسکی شکل از جنس آلیاژ نیکل-کروم تهیه شد. سطح باند شونده در تمام نمونه ها توسط ذرات اکسید آلومینیوم µ50 سندبلاست شدند. نمونه ها به 4 گروه 10تایی تقسیم و به صورت زیر آماده سازی شدند: 1- سندبلاست با اکسید آلومینیوم (A.A)؛ 2- سندبلاست با پودر (CJ) Cojet؛ 3- سطح نمونه ها با پودر Cojet پوشیده شده و لیزر Nd:YAG  به سطح تابیده شد (CJ-Lased-Nd:YAG)؛ 4- سطح نمونه ها با پودر Cojet پوشیده شده و لیزر CO2  به سطح تابیده شد (CJ-Lased-CO2). سپس کامپوزیت رزین بر روی سطح نمونه ها کیور شد. بعد از ترموسایکل، استحکام باند برشی نمونه ها توسط دستگاه یونیورسال اندازه گیری شد. نوع شکست در زیر میکروسکوپ نوری مشاهده شد و دو نمونه از هر گروه با SEM و WDX بررسی شد. داده ها با استفاده از آزمون های ANOVA و Tukey آنالیز شدند (α=0.05). یافته ها: مقدار استحکام باند در گروه CJ به طور معنی داری از سایر گروه ها بالاتر بود (001/0P<). بین مقادیر استحکام باند برشی گروه های A.A، CJ-Lased-Nd:YAG و CJ-Lased-CO2تفاوت معنی داری وجود نداشت (05/0